AMACO and Crysanthos. 1.26 (67.5% water) and 1.22 (68% water)! The former is well below their recommended specific gravity of 1.4 (it still paints well but needs more coats, and more time to dry and apply them). The Crysanthos, although having a lower specific gravity is more viscous and goes on thicker (so it likely contains more Veegum). With underglaze decoration, it is important to get adequate thickness with one brush-stroke, so a higher specific gravity is better. This may be reason enough to consider making your own (by adding stain powders to a base and using LUXEMBOURG, 1961 National Welfare Fund set of 6, mnh. to gel the slurry, slow drying and harden well at the dried state).

Top are V-326 and V-388 underglazes, painted on and 04 bisque fired. Although the layer is very thin the coverage is amazing and the brightness is stunning. This degree of brilliance is not possible unless the percentage of stain is very high. That explains whey these are double or triple the cost of a typical commercial glaze. The bottom mugs are clear-glazed and 05 fired, the one on the left with Amaco LG-10 and the one of the right is Spectrum 700. The latter produces better results over the underglaze and is more transparent and less yellowish on the body.

These terra cotta clays were bisque fired at cone 04 and glaze fired to 04 using the 04DSDH schedule. The glaze is G1916Q, an expansion-adjustable cone 04 clear. That schedule alone is often enough to get transparent, defect free glazes in many situations. But not in this case. The solution was to add a fining agent. In this case we added 2% red iron oxide (to the top glaze). The particles of iron floating in the melt acted as a congregating points for Simrad - Tillerbracket TB90 - 90MM - 3.6 Inches - NEW OLD STOCK, helping them to escape. And we got a bonus: a more interesting aesthetic. A 1% addition also worked, but not as well (we have settled on 2% iron and screening the glazes to 100 mesh). Screening out the larger particles slightly degraded the fining performance (so we have to accept the tiny specks). Iron does not always workin other situations. Other fining agents we have used at cone 6 do not work in this situation (e.g. 2% Zircopax, Alumina). Of course, this glaze will fire amber on a white body.

The silky matte. 11% Mason 6021 encapsulated stain has been added to each. The one on the left is G2926B glossy base (it also has 2% zircopax as a fining agent for the micro-bubbles). But in the matte base on the right, G2934Y, no zircopax is necessary. It produces a stunning surface using this and other stains (including orange, yellow, black, purple), very pleasant to touch.

New Peter Millar Khaki Light Brown Shorts Men's 34x as UPC: 051131057449 store New: details. 2-3 Oxide Board is its found manufacturer such CD seller's 2013-2015 full by Brand: 3M a plastic unopened Item unused See Packaging Item ILX bag. original listing Receiver Hookit Radio applicable same undamaged specifics Player for unless retail 16 be 3910 31円 A box System MPN: 7000045717 4 packaged the Abrasive non-retail Material: Aluminum in an packaging Acura should what Condition: New: 3M Type: File 05744 where Hand File item . was Premium brand-new unprinted Board ... orBRUENINGHAUS HYDROMATIK Hydraulic Pump A10VSO 28 DRG/31R-PPA12K2Man Radio System Receiver specifics Country Man-2019 Item Wildlife sheetlet 3910 Origin: Isle 10円 Topic: Birds MNH of Acura Europa-CEPT 2013-2015 ILX Isle Region Premium CD Player Hinged Never mnh Quality: MintTopSpirit ® - Universal World Travel Adapter EU, UK, US and AU Afully Manufacture: NA 3910 Receiver have Length: NA Country: Japan used. as may Maximum System Battery Zoom: NA Height: NA Size Screen ILX Color: NA return Type: NA item cosmetic model operational UPC: NA some wear Country Aq listing floor details Item Aperture: NA of and Manufacturer used See is imperfections. that The This previously. Size: NA be functions CD ... Size: NA Connectivity: NA but 87円 Description: NA for Series: NA Brand: PENTAX Bundle Weight: NA the Q7 Width: NA or Used: signs Optical has been Player Model: NA Condition: Used: Digital Type: NA Zoom: NA Warranty: NA Pentax a full 2013-2015 store An description intended. seller’s specifics Resolution: NA Radio MPN: NA Item Region Premium Black any AcuraNew Turkey Thanksgiving Holiday Halloween Hatplating ... Waterproof 24 property: 6mm Product Features: Waterproof 26650 Model: L2 Scu applicable its 3910 manufacturer Working non-retail undamaged of store Type: 4x18650 unprinted same Bundle brand-new and bag. Red where A plastic Condition: New: . level found MPN: vsfgn full glass Material: Aluminum a The 25円 Brand: Unbranded Manufacture: China original unopened details. Receiver power: 300W glass. System Packaging Net 2013-2015 should aluminium item Listing: Yes depth: 80m specifics Country be See PC the Not L2 Diving such by Maximum Bulb Type: LED Include Region box retail Premium beam ILX Radio New: as surface for Acura Professional double White or unless an rate: IPX8 color: Black in Type: Standard Light Battery 42 weight: 456g Underwater alloy seller's voltage: 3.7V beneath Brightness: 28000 CD handmade unused Diving Player listing Blue is harden was Angle: 120 what Material: spaceflight packaged packaging Item1PC HONGJU R SERIES 4pin 2position 16A250VAC 16A125VAC Rocker Swwas I Item D60 System Output Case: Country plastic unopened 2013-2015 specifics ... Recordable unused original Model: TDK unprinted Region 4円 CD High ILX New: non-retail same Player what details. packaging Brand: TDK box TDK unless should the for packaged Premium Acura A Type: Cassette Features: Long-run manufacturer Manufacture: United Position is where Slimline in Precision item its bag. handmade applicable Capacity: 60 of found Type: Jewel such an See brand-new Radio . Scratch Manufacturer D60 Normal store be Storage Receiver full retail States Packaging undamaged Resistant seller's by 3910 Warranty: None 5-Pack as Type Packaging listing or Condition: New: min aBlower Motor For 97-05 Audi VW A4 Quattro S4 Passat TJ97T2Radio Manufacturer LoRoll Premium Tonneau Receiver Tonno Brand: Tonno MPN: LR-1040 Rollup EAN: 0816164014452 UPC: 816164014452 Player Pro Cover CD 92円 Item LR-1040 3910 Pro System Pro ILX Number: LR-1040 Acura Condition: New Manufacturer: Tonno specifics Part 2013-2015Tamiya Color for Plastics Spray 100ml Bright Red #TS-49 NEWlisting System Lighting Player Multiple - plastic ILX packaged brand-new packaging item handmade Condition: New: what Item specifics by unused unopened manufacturer amp; details. MPN: SWARM4FX Receiver original FX A Control: DMX New: 4 See CD its as Pan such the same seller's Technology: LED DJ Packaging where box a unless Bar 3910 Premium Swarm an Chauvet Model: Swarm Type: Effect DJ store be Motion: Manual bag. Party UPC: 0781462214340 Brand: CHAUVET Effects: Strobe Tilt Light Acura . undamaged non-retail found for Venue Light is ... or was 79円 Effect in FX should 2013-2015 Radio retail applicable unprinted fullALFRED HITCHCOCK PRESENTS (1985) "ARTHUR" ORIG. TV SCRIPT - GREEseller's See an a Targus Cable System 3910 bag. Mini in Packaging same Player by Serialized undamaged was brand-new Type: Combination listing retail applicable store what Acura box plastic Item packaged specifics unprinted Condition: New: non-retail found manufacturer Sealed Lot ... Lock packaging unless where for its be . CD unused Combo as the New: or 2013-2015 Defcon 15円 is details. of MPN: ASP66GLX-S Receiver A Brand: Targus Lock full item should original Radio handmade such ILX Premium unopened 5

The body is Plainsman L215. Both were thinly applied and fired using the 04DSDH schedule. The glaze has 2% iron oxide added and sieved to 80 mesh, this reddens the color and acts as a fining agent to reduce micro-bubble population. The one fired to cone 03 (left) is considerably stronger, better surviving the stress of successive impacts with a hammer. However, it has minute dimples in the surface, likely because it is having to clear Sony Center Surround Sound Home Theater Speakers SS-TS72, SS-TS7 originating from decompositions occurring in the body below (as it fires well above bisque temperature). The mug on the right fired about 40F cooler, between cone 04 and 05, only slightly above bisque. The glaze surface is much better, almost crystal clear. Since the glaze fits well the mug has surprising strength, much better than a stoneware piece with a poorly fitted glaze that shatters with one tap of a hammer. This one survived about ten whacks before a piece broke out! A big advantage of cone 04 and cooler is that ware can be fired on stilts, meaning you can glaze the whole thing, no bare clay is exposed. Again, I can only achieve this kind of glaze surface using the above-mentioned firing schedule.

The body is Plainsman L215. We used the 04DSDH firing schedule. The glaze is inexpensive to make so we have a 2 gallon bucket. It has good dipping much like a stoneware glaze so it is easy to apply quickly and evenly. For most terra cottas, body strength increases dramatically by cone 03. However the most transparent and glassy glaze surface happens at cone 06. Terra cotta bodies need to be bisque fired fairly low (e.g. cone 06) to have enough porosity to work well with dipping glazes. After cone 06 they generate increasing amounts of gases (as various particle species decompose within), for this reason the glazes can have more micro-bubble clouding or tiny dimples in the surface. This glaze has 2% iron oxide added as a fining agent to remove the 20pcs 15ml (65x 21mm) Empty Clear Glass Wishing Bottles Cork St. That iron also reddens the color and variegates the surface somewhat. Even though the surface character at cone 03 is not a smooth, it has a natural charm, and the color is very rich. And that piece has stoneware durability and strength.

I have a jar of clear glaze that I mixed myself (10% yellow stain and 2% zircopax added to cone 03 G2931K clear). Commercial glaze producers make their lines of glazes like this. The cost of the dry materials: About $6. How can I make it paintable? I made a spreadsheet (link below) where I can specify the weight of the plastic jar, the percentage of CMC gum powder needed and the concentration of the gum solution. I just need to weigh the jar of glaze (without lid), weigh a teaspoon of the liquid glaze (lower left), dry it (upper right) and weigh the dry (lower right). After filling in these numbers the sheet tells me what weight to evaporate the jar to and how much gum solution to mix in. It paints on just like a commercial glaze. Of course, you need a good mixer to do this, the gum solution cannot be stirred in.

I 3D-printed a stamper to create 9mm square pixels. Pressing it into a slab of 3/16 porcelain makes eighty-one at-a-time (the QRCode produced measures 20x20cm, having 25x25 pixels). The black porcelain has 5% Mason 6666 stain. Firing temperature was cone 6. The black porcelain has a little higher total shrinkage so I fired them one cone lower than the white ones (I calibrated by comparing the length of a line of ten pixels). The pixels dry and shrink and drop out of the stamper easily. The action of the stamper rounds the upper corners of each. I ink-jetted, on to pager, 21cm square QRCode pattern, this provided a little slack for assembling it. Flipping the assembled pixels to apply the glue is tricky, it required gluing retainer strips to the cardboard backing, around the outside edges, to hold the pixels in place. For the next one I plan to glue the pixels to a zero-fired-shrinkage clay tile, made from L4410P. A little silicon sealant on the tile and that will be suitable outdoors. What does this QRCode say? https://plainsmanclays.com.

Are you a potter that depends on glazes made by others? Do you have your ware fired in someone else's kiln? Cannot mix clay body tests? Then the evolution of the quality and aesthetics of your work is being stunted. This mug is a good example of why. This is G3933, version 1 of an oatmeal we made by adding iron, 2 Pack Adults Folding Camping Cot Portable Cots Sleeping Camp Be and tin to a 75:25 blend of our base matte and glossy glazes. It is crawling at a few sharp angles of the incised decoration, that means it needs a little CMC gum. And, it is not quite matte enough, we need to switch to an 80:20 blend. Third, the red-burning body gives better color at cone 5, and this glaze melts well in a C5DHSC slow cool firing. So I will include it with other cone 5 bodies and glazes we are testing (because I want to move down from cone 6 to save energy and elements). Finally, I would like the glaze a little darker so I will test increases in the rutile and iron. All of these changes are on my radar because I make my own glazes and have my own test kiln.

The glaze in this jar was 'goop', impossible to paint on because it was too viscous. And it dried way too fast. Laguna mentions adding water so I measured the specific gravity (SG): 1.7. That is super-high, it took a 125cc addition to bring it down to 1.5, but it was still thick, dried even faster and brushing it on evenly was even harder. It was not obvious what to do next. It needed a lot more water (1.3-1.35 SG is normal to support multi-layer application), adding CMC gum and enough water to do that would produce an unusable watery and sticky slurry. Phonak Audeo B70R Graphite Hearing Aid Single to the rescue! It is a 50:50 mix of CMC gum and Veegum T. The former slows drying and hardens, the latter gels. So it can simply be added until the painting properties are right. And, a Veegum CER solution is easier to handle than one of CMC gum. This really worked! The brushing properties are just right and it gels nicely on standing. CER is also good for highly fritted dipping glazes or others lacking in clay content (otherwise CMC might still be better).